MIM Powders

Our company pioneered and developed the water-gas combining atomization process for MIM powder production in China. Now we possessed gas atomization , water atomization , water and gas combination equipment, and can provide all kinds of stainless steel powders, low alloy steel powders, cobalt-based and nickel-based powders.

Chat with us

Leave a message

Technical information

Features
Typical Applications
Technical Specifications

Features

Our MIM powders have the characteristics of low oxygen content, regular morphology, high tap density, stable particle size distribution and chemical composition. The maximum weight of 5 tons per batch is convenient for customers to use. The advanced MIM evaluation laboratory can fully guarantee the consistency of product quality, and the product access to the customers recognition.

Typical Applications

MIM powder is mainly used as raw material for metal injection molding（MIM） to make various small parts with complex structures，such as? mobile phone SIM card slot, smart electronic watch shell and other products.

Technical Specifications

Products	Cr	Ni	Mo	Si	Mn	Nb	Cu	Co	Oxygen Content （PPM）	Tap Density （g/cm³）	?Laser Particle Size
Products	Cr	Ni	Mo	Si	Mn	Nb	Cu	Co	Oxygen Content （PPM）	Tap Density （g/cm³）	D10	D50	D90?
316L(gas）	16-18	11-14	2-3	<1.0	<1.5				500	4.95	5.1	13.7	28.2
316L	16-18	11-14	2-3	<1.0	<1.5				2900	4.75	3.06	9.61	23.33
17-4PH	15.5-17.5	3-5	<0.5	<1.0	<1.0	0.15-0.45	3.5		3100	4.70	3.47	9.87	24.37
440C	16-18	<0.2	0.4-0.8	<1.0	<1.0				1500	4.40	3.6	10.92	26.90
420L	12-14			<1.0	<1.0				2000	4.40	3.11	9.83	22.62
304L	18-20	8-12	<0.2	<1.0	<1.5				3500	4.80	3.06	9.97	25.82
4605		1.5-2.5	0.2-0.5	<1.0					3500	4.40	3.75	10.80	25.78
8620	0.5-1.0	0.5-1.0	<0.5						3000	4.63	3.25	9.46	23.07
HK30	24-27	19-22	<0.5	0.75-1.4	<1.5	1.2-1.5	<0.3		3400	4.20	3.24	8.74	20.88
4J29	<0.2	28-30	<0.2	≤0.3	≤0.5		<0.15	16-18	2500	5.10	3.16	9.87	23.42
1J85		79-81	4.8-5.0	0.15-0.3	0.3-0.6		<0.2		1600	5.10	4.01	10.24	23.69
F75	28-32		6.8	≤0.5	≤0.5			60-62	3200	5.10	2.98	8.89	21.68

Powder Sintering Properties

Products	Carbon Content	Sintering Temperature （℃ ）	Sintering Density （g/cm3 ）	Shrinkage %	Tensile Strength （MPa）	Yield Strength （Mpa）	Hardness (HRB)?	Elongation %?
316L(gas）	<0.03	1360-1380	≥7.9	1.173	547	193	≥69	56.5
316L	<0.03	1360-1380	≥7.85	1.167	530	186	≥65	54.5
17-4PH	<0.07	1280-1320	≥7.6	1.165	975	730	≥28（HRC)	5
440C	1.2-1.4	1230-1240	≥7.5	1.165	1137	538	≥55（HRC)	1.7
420L	0.15-0.45	1320-1360	≥7.6	1.165	800	650	≥600（HV)	5
304L	<0.03	1360-1380	≥7.75	1.165	530	186	≥65	35
4605	0.4-0.6	1250-1280	≥7.5	1.185	700	500	≥70	11
8620	<0.2	1250-1280	≥7.5	1.165	445	210	≥45	30
HK30	0.35-0.65	1310-1330	≥7.6	1.165	782	436	≥80	18
4J29	<0.03	1330-1380	≥8.0	1.162	480	280	≥180（HV)	38
F75	<0.035	1330-1380	≥8.0	1.165	1200	850	≥280（HV)	12